"Abrasion-resistant POE 0210 Toughened Elastomer High Temperature Resistance" parameter description

In stock:	Yes	Authentication:	Standard Level
Type:	POE	Grade:	0210
Processing Level:	Injection grade, hollow grade, coating grade, wire drawing grade, extrusion grade	Feature Level:	Toughening grade, thermal stability, high temperature resistance
Usage Level:	General purpose, food grade, auto parts, pipe grade	Model:	0210
Specifications:	25KG	Trademark:	Standard Level
Packaging:	Standard Level

Detailed introduction of "wear-resistant POE 0210 toughened elastomer high temperature resistance"

Variety: POE丨0210

Manufacturer: Exxon Mobil

Specifications

Spec Level	Other Other Injection	Appearance Color
Use of the material
Notes

Technical parameters

Performance items		Test Condition [Status]	Test Method	Test Data	Data Unit
Basic performance	Hardness 2	Shore D,15 sec	ASTM D-2240	43
	Hardness 2	Shore A,15 sec	ASTM D-2240	85
	Melt Index		ASTM D-1238	10.0	g/10 min
	Melt Flow Rate		ASTM D-1238	25	g/10 min
	Density		ExxonMobil Method	0.902	g/cm3
	Haze 2		ASTM D-1003	84@50mils	%
Physical Properties	Flexural Modulus	1% secant	ASTM D-790	11.100 (76.6)	psi(MPa)
	Impact Strength	-40℃	ASTM D-256	No Break	ft-lb/in(J/m)
	Stretch Ratio	@Break	ASTM D-638	No Break	%
	Tensile Strength 3	@Break	ASTM D-638	No Break	psi(MPa)
	Impact Strength	23℃	ASTM D-256	No Break	ft-lb/in(J/m)
Thermal performance	Vicat softening point 2	200g	ASTM D-1525	183.4 (84.1)	℉(℃)
	Melt Temperature		ExxonMobil Method	205(96.0)	℉(℃)
Other features	Mooney Viscosity ML(1+4)	125℃	ASTM D-1646	4.6	Torgue Units
	Tear Strength		ASTM D-624	423 (74.1)	lb/in(kN/m)
	tensile strength	@Peak	ASTM D-412	No Break	psi(MPa)
	tensile stress 5	@Elongation	ASTM D-412	914(6.3)	psi(MPa)
	Stretch Ratio	@Break	ASTM D-412	No Break	%
	tensile stress 5	@300% Elongation	ASTM D-412	972(6.7)	psi(MPa)